Béléng anu panas panas (GB / T9437-1988)

kelas

Ngaran toko

Komposisi kimia (fraksi massa) (%)

C

Si

Mn

P

S

Ceun

Al

Kirang ti atanapi sami

Beusi beusi tuang

Rtcr

3.0-3.8

1.5-2.5

1.0

0.20

0.12

0.50-1.00

-

Rtc2

3.0-3.8

2.0-3.0

1.0

0.20

0.12

>1.00-2.00

-

Rtcr16

1.6-2.4

1.5-2.2

1.0

0.10

0.05

15.00-18.00

-

Rti5

2.4-3.2

4.5-5.5

0.8

0.20

0.12

0.50-1.00

-

Beusi tuang tuang tuang

Rtqsi4

2.4-3.2

3.5-4.5

0.7

0.10

0.03

-

-

Rtqsi4mo

2.7-3.5

3.5-4.5

0.5

0.10

0.03

Mo: 0,3-0.7

-

Rtqsi5

2.4-3.2

>4.5-5.5

0.7

0.10

0.03

-

-

Rtqal4si4

2.5-3.0

3.5-4.5

0.5

0.10

0.02

-

4.0-5.0

Rtqal5S5

2.3-2.8

>4.5-5.2

0.5

0.10

0.02

-

>5.0-5.8

Rtqal22

1.6-2.2

1.0-2.0

0.7

0.10

0.03

-

20.0-24.0

Ngaran toko

Kakuatan Tensile tina B / MPA
Langkung ageung atanapi sami

Hardness Hbs

Ngaran toko

Kakuatan Tensile tina B / MPA
Langkung ageung atanapi sami

Hardness Hbs

Rtcr

200

189-288

Rtqsi4mo

540

197-280

Rtc2

150

207-288

Rtqsi5

370

228-302

Rtcr16

340

400-450

Rtqal4si4

250

285-341

Rti5

140

160-270

Rtqal5S5

200

302-363

Rtqsi4

480

187-269

Rtqal22

300

241-364

Ngaran toko

Kakuatan tensile tina b / mpa dina suhu ieu (gelar)

Ngaran toko

Kakuatan tensile tina b / mpa dina suhu ieu (gelar)

500

600

700

800

900

500

600

700

800

900

Rtcr

225

144

-

-

-

Rtqsi4mo

-

-

101

46

-

Rtc2

243

166

-

-

-

Rtqsi5

-

-

67

30

-

Rtcr16

-

-

-

144

88

Rtqal4si4

-

-

-

82

32

Rti5

-

-

41

27

-

Rtqal5S5

-

-

-

167

75

Rtqsi4

-

-

75

35

-

Rtqal22

-

-

-

130

77